Polydimethylsiloxane Polymerized Emulsions for Acoustic Materials Prepared Using Reactive Triblock Copolymer Surfactants.

Porous polymers have interesting acoustic properties including wave dampening and acoustic impedance matching and may be used in numerous acoustic applications, e.g., waveguiding or acoustic cloaking. These materials can be prepared by the inclusion of gas-filled voids, or pores, within an elastic polymer network; therefore, porous polymers that have controlled porosity values and a wide range of possible mechanical properties are needed, as these are key factors that impact the sound-dampening properties. Here, the synthesis of acoustic materials with varying porosities and mechanical properties that could be controlled independent of the pore morphology using emulsion-templated polymerizations is described. Polydimethylsiloxane-based ABA triblock copolymer surfactants were prepared using reversible addition-fragmentation chain transfer polymerizations to control the emulsion template and act as an additional cross-linker in the polymerization. Acoustic materials prepared with reactive surfactants possessed a storage modulus of ∼300 kPa at a total porosity of 71% compared to materials prepared using analogous nonreactive surfactants that possessed storage modulus values of ∼150 kPa at similar porosities. These materials display very low longitudinal sound speeds of ∼35 m/s at ultrasonic frequencies, making them excellent candidates in the preparation of acoustic devices such as metasurfaces or lenses.

Synthesis and Applications of Elastomeric Polymerized High Internal Phase Emulsions (PolyHIPEs).

Polymer foams (PFs) are among the most industrially produced polymeric materials, and they are found in applications including aerospace, packaging, textiles, and biomaterials. PFs are predominantly prepared using gas-blowing techniques, but PFs can also be prepared from templating techniques such as polymerized high internal phase emulsions (polyHIPEs). PolyHIPEs have many experimental design variables which control the physical, mechanical, and chemical properties of the resulting PFs. Both rigid and elastic polyHIPEs can be prepared, but while elastomeric polyHIPEs are less commonly reported than hard polyHIPEs, elastomeric polyHIPEs are instrumental in the realization of new materials in applications including flexible separation membranes, energy storage in soft robotics, and 3D-printed soft tissue engineering scaffolds. Furthermore, there are few limitations to the types of polymers and polymerization methods that have been used to prepare elastic polyHIPEs due to the wide range of polymerization conditions that are compatible with the polyHIPE method. In this review, an overview of the chemistry used to prepare elastic polyHIPEs from early reports to modern polymerization methods is provided, focusing on the applications that flexible polyHIPEs are used in. The review consists of four sections organized around polymer classes used in the preparation of polyHIPEs: (meth)acrylics and (meth)acrylamides, silicones, polyesters and polyurethanes, and naturally occurring polymers. Within each section, the common properties, current challenges, and an outlook is suggested on where elastomeric polyHIPEs can be expected to continue to make broad, positive impacts on materials and technology for the future.

Synthesis of patterned polyHIPE-hydrogel composite materials using thiol-ene chemistry.

Elastomeric materials combining multiple properties within a single composite are highly desired in applications including biomaterials interfaces, actuators, and soft robotics. High spatial resolution is required to impart different properties across the composite for the intended application, but many techniques used to prepare these composites rely on multistep and complex methods. There is a need for the development of simple and efficient platforms to design layered composite materials. Here, we report the synthesis of horizontally- and vertically-patterned composites consisting of PDMS-based polymerized high internal phase emulsion (polyHIPE) porous elastomers and PDMS/PEG hydrogels. Composites with defined interfaces that were mechanically robust were prepared, and rheological analysis of the polyHIPE and hydrogel layers showed storage moduli values of âˆ¼ 35 kPa and 45 kPa respectively. The compressive Young's Modulus and maximum strain of the polyHIPEs were dependent on the thiol to ene ratio in the formulation and obtained values ranging from 6 to 25 kPa and 50-65% respectively. The mechanical properties, total porosity of the polyHIPE, and swelling ratio of the hydrogel were unaffected by the patterning technique compared to non-patterned controls. PolyHIPE-hydrogel composite materials having up to 7-different horizontally pattered layers could be prepared that could expand and contract up hydration and drying.

Hydrophilic Micro- and Macroelectrodes with Antibiofouling Properties for Biomedical Applications.

Implantable neural electrodes are generally used to record the electrical activity of neurons and to stimulate neurons in the nervous system. Biofouling triggered by inflammatory responses can dramatically affect the performance of neural electrodes, resulting in decreased signal sensitivity and consistency over time. Thus, long-term clinical applications require electrically conducting electrode materials with reduced dimensions, high flexibility, and antibiofouling properties that can reduce the degree of inflammatory reactions and increase the lifetime of neural electrodes. Carbon nanotubes (CNTs) are well known to form flexible assemblies such as CNT fibers. Herein, we report the covalent functionalization of predefined CNT fiber and film surfaces with hydrophilic, antibiofouling phosphorylcholine (PC) molecules. The electrochemical and spectroscopic characteristics, impedance properties, hydrophilicity, and in vitro antifouling nature of the functionalized CNT surfaces were evaluated. The hydrophilicity of the functionalized CNT films was demonstrated by a decrease in the static contact angle from 134.4° ± 3.9° before to 15.7° ± 1.5° after one and fully wetting after three functionalization cycles, respectively. In addition, the extent of protein absorption on the functionalized CNT films was significantly lower than that on the nonfunctionalized CNT film. Surprisingly, the faradic charge-transfer properties and impedance of the CNT assemblies were preserved after functionalization with PC molecules. These functionalized CNT assemblies are promising for the development of low-impedance neural electrodes with higher hydrophilicity and protein-fouling resistance to inhibit inflammatory responses.

Heparin Mimic Material Derived from Cellulose Nanocrystals.

This study analyzes and evaluates the use of cellulose nanocrystals (CNCs), stiff nanosized natural materials that have been modified to mimic heparin. These CNCs are simple polysaccharides with a similar backbone structure to heparin, which when modified reduces coagulation and potentially the long-term effects of solution-based anticoagulants. Thus, CNCs represent an ideal foundation for generating materials biocompatible with blood. In this study, we developed a biocompatible material that inhibits blood clotting through surface functionalization to mimic heparin. Surface chemistry of CNCs was modified from "plain" CNCs (70 mmol SO3-/kg) to 500 mmol COO-/kg (TEMPO-oxidized CNCs) and 330 mmol SO3-/kg CNCs (sulfonated CNCs). Platelet adherence and blood assays show that changes in functionalization reduce coagulation. By utilizing and modifying CNCs reactive functional groups, we create a material with unique and favorable mechanical properties while also reducing clotting.

Reversibly Softening and Stiffening Organogels Using a Wavelength-Controlled Disulfide-Diselenide Exchange.

Wavelength-dependent light-responsive seleno-sulfide dynamic covalent bonds were used to prepare organogels with reversible changes in stiffness. The disulfide cross-link organogels prepared from norbornene-terminated poly(ethylene glycol) (PEG-diNB) and poly(2-hydroxypropyl methacrylate-stat-mercaptoethyl acrylate) (PEG-diNB-poly(HPMA-stat-MEMA)) polymers underwent exchange reactions with 5,5'-diselenide-bis(2-aminobenzoic acid) upon irradiation with UV light. Following irradiation with visible light, the seleno-sulfide bonds were cleaved, reforming disulfide cross-links and the 5,5'-diselenide-bis(2-aminobenzoic acid). Reduction in G' with disulfide-diselenide exchange was consistent with that observed following a thiol-disulfide exchange reaction. Recovery of G' upon disulfide bond formation was 85-95% of the initial value in the as-prepared gel over five cycles of bond cleaving and reformation. This initial study shows the potential of the wavelength-controlled disulfide-diselenide chemistry to develop light-responsive reversible organogels. These organogels have the potential to be used in functional materials such as polymeric actuators or biomimetic soft robotics.

Fabrication of single-chain nanoparticles through the dimerization of pendant anthracene groups via photochemical upconversion.

We report on the use of visible light as the driving force for the intramolecular dimerization of pendant anthracene groups on a methacrylic polymer to induce the formation of single-chain nanoparticles (SCNPs). Using a 532 nm green laser light source and platinum octaethylporphyrin as a sensitizer, we first demonstrated the use of TTA-UC to dimerize monomeric anthracene, and subsequently applied this concept to dilute poly((methyl methacrylate)-stat-(anthracenyl methacrylate)) samples. A combination of triple-detection size-exclusion chromatography, atomic force microscopy, and UV-visible spectroscopy confirmed the formation of the SCNPs. This report pioneers the use of TTA-UC to drive photochemical reactions in polymeric systems, and showcases the potential for TTA-UC in the development of nanoobjects.

Stimuli-Responsive Self-Immolative Polymer Nanofiber Membranes Formed by Coaxial Electrospinning.

The first self-immolative polymer (SIP) nanofiber membrane is demonstrated in this report, in which the immolation can be triggered by external stimulus. Electrospun SIP/polyacrylonitrile (PAN) fibers provide depolymerization that is ∼25 times quicker and more responsive (i.e., immolation) than that of a cast film in the triggering condition. Depolymerization of SIP in the SIP/PAN blended fiber membrane results in the transition of the surface properties from hydrophobic (∼110°) to hygroscopic (∼0°). Triggered release of encapsulated functional molecules was demonstrated using coaxially electrospun fiber membrane made of a SIP/PAN blend sheath and polyvinylpyrrolidone/dye core. Coaxial fibers with the SIP/PAN sheath provide minimal release of the encapsulated material in nontriggering solution, while it releases the encapsulated material instantly when the triggering condition is met. Its versatility has been strengthened compared to that of non-SIP coaxial fibers that provide no triggering reaction by external stimulus.

Photodynamic Inactivation of Multidrug-Resistant Staphylococcus aureus Using Hybrid Photosensitizers Based on Amphiphilic Block Copolymer-Functionalized Gold Nanoparticles.

Multidrug-resistant Staphylococcus aureus (MRSA) has become one of the major causes of various infections, leading to morbidity in both healthy and immune-compromised populations worldwide. Herein, we report a novel type of hybrid photosensitizer based on amphiphilic block copolymer-functionalized gold nanoparticles. The design of the nanoparticles provides a facile means to incorporate hydrophobic photosensitizing molecules for use in aqueous media. The hybrid photosensitizers display greatly enhanced singlet oxygen generation and outstanding photodynamic inactivation (PDI) efficacy against MRSA under light illumination. These hybrid photosensitizers greatly improve the effectiveness of PDI against MRSA while not involving antibiotics.

pH-Degradable Mannosylated Nanogels for Dendritic Cell Targeting.

We report on the design of glycosylated nanogels via core-cross-linking of amphiphilic non-water-soluble block copolymers composed of an acetylated glycosylated block and a pentafluorophenyl (PFP) activated ester block prepared by reversible addition-fragmentation (RAFT) polymerization. Self-assembly, pH-sensitive core-cross-linking, and removal of remaining PFP esters and protecting groups are achieved in one pot and yield fully hydrated sub-100 nm nanogels. Using cell subsets that exhibit high and low expression of the mannose receptor (MR) under conditions that suppress active endocytosis, we show that mannosylated but not galactosylated nanogels can efficiently target the MR that is expressed on the cell surface of primary dendritic cells (DCs). These nanogels hold promise for immunological applications involving DCs and macrophage subsets.

Development of Non-Viral, Trophoblast-Specific Gene Delivery for Placental Therapy.

Low birth weight is associated with both short term problems and the fetal programming of adult onset diseases, including an increased risk of obesity, diabetes and cardiovascular disease. Placental insufficiency leading to intrauterine growth restriction (IUGR) contributes to the prevalence of diseases with developmental origins. Currently there are no therapies for IUGR or placental insufficiency. To address this and move towards development of an in utero therapy, we employ a nanostructure delivery system complexed with the IGF-1 gene to treat the placenta. IGF-1 is a growth factor critical to achieving appropriate placental and fetal growth. Delivery of genes to a model of human trophoblast and mouse placenta was achieved using a diblock copolymer (pHPMA-b-pDMAEMA) complexed to hIGF-1 plasmid DNA under the control of trophoblast-specific promoters (Cyp19a or PLAC1). Transfection efficiency of pEGFP-C1-containing nanocarriers in BeWo cells and non-trophoblast cells was visually assessed via fluorescence microscopy. In vivo transfection and functionality was assessed by direct placental-injection into a mouse model of IUGR. Complexes formed using pHPMA-b-pDMAEMA and CYP19a-923 or PLAC1-modified plasmids induce trophoblast-selective transgene expression in vitro, and placental injection of PLAC1-hIGF-1 produces measurable RNA expression and alleviates IUGR in our mouse model, consequently representing innovative building blocks towards human placental gene therapies.

Triplet-triplet annihilation upconversion from rationally designed polymeric emitters with tunable inter-chromophore distances.

We report an investigation of triplet-triplet annihilation upconversion (TTA-UC) based on polymeric emitters with tunable inter-chromophore distances. Poly[(9-anthrylmethyl methacrylate)-co-(methyl methacrylate)] (poly(AnMMA-co-MMA)) with different percentages of AnMMA was synthesized using reversible addition-fragmentation chain transfer (RAFT) polymerization, and used as an emitter in association with platinum octaethylporphyrin as a sensitizer to form TTA-UC systems. It is observed that the TTA-UC intensity first increases with increasing AnMMA percentage in the polymers then decreases, and ultimately disappears, upon further increasing the AnMMA percentage. The results shed light on the key factors affecting TTA-UC in polymers, and have implications for the design of polymer-based TTA-UC systems.

Synthesis and anticoagulant activity of polyureas containing sulfated carbohydrates.

Polyurea-based synthetic glycopolymers containing sulfated glucose, mannose, glucosamine, or lactose as pendant groups have been synthesized by step-growth polymerization of hexamethylene diisocyanate and corresponding secondary diamines. The obtained polymers were characterized by gel permeation chromatography, nuclear magnetic resonance spectroscopy, and Fourier transform infrared spectroscopy. The nonsulfated polymers showed similar results to the commercially available biomaterial polyurethane TECOFLEX in a platelet adhesion assay. The average degree of sulfation after reaction with SO3 was calculated from elemental analysis and found to be between three and four -OSO3 groups per saccharide. The blood-compatibility of the synthetic polymers was measured using activated partial thromboplastin time, prothrombin time, thrombin time, anti-IIa, and anti-Xa assays. Activated partial thromboplastin time, prothrombin time, and thrombin time results indicated that the mannose and lactose based polymers had the highest anticoagulant activities among all the sulfated polymers. The mechanism of action of the polymers appears to be mediated via an anti-IIa pathway rather than an anti-Xa pathway.

Stimuli-responsive surfaces using polyampholyte polymer brushes prepared via atom transfer radical polymerization.

The synthesis of AB diblock copolymer polyampholyte polymer brushes of the type Si/SiO2//poly(acrylic acid-b-vinyl pyridine) prepared using atom transfer radical polymerization is reported. Both 2- and 4-vinyl pyridine have been used. The diblock polyampholyte polymer brushes demonstrate stimuli-responsive behavior with respect to pH, showing both polyelectrolyte and polyampholyte effects. Furthermore, we have quaternized the 4-vinyl pyridine segments to form a mixed weak/strong, or annealed/quenched, polyelectrolyte system. The quaternized polymer brush exhibits different pH-responsive behavior, with decreasing film thickness being observed with increasing pH.

Stimuli-responsive polyelectrolyte polymer brushes prepared via atom-transfer radical polymerization.

We present an account of our research into polyelectrolyte polymer brushes that are capable of acting as stimuli-responsive films. We first detail the synthesis of poly(acrylic acid) polymer brushes using ATRP in a "grafting from" strategy. Significantly, we employed a chemical-free deprotection step that should leave the anchoring ester groups intact. We have demonstrated how these polymer assemblies respond to stimuli such as pH and electrolyte concentration. We have used poly(acrylic acid) polymer brushes for the synthesis of metallic nanoparticles and review this work. We have used XPS, ATR-FTIR, and AFM spectroscopy to show the presence of silver and palladium nanoparticles within polymer brushes. Finally, we report the synthesis of AB diblock polyampholyte polymer brushes that represent an extension of polyelectrolyte polymer brushes.

Facile, controlled, room-temperature RAFT polymerization of N-isopropylacrylamide.

Poly(N-isopropyl acrylamide) is a thermoresponsive polymer that has been widely investigated for drug delivery. Herein, we report conditions facilitating the controlled, room-temperature RAFT polymerization of N-isopropylacrylamide (NIPAM). The key to success is the appropriate choice of both a suitable RAFT chain transfer agent (CTA) and initiating species. We show that the use of 2-dodecylsulfanylthiocarbonylsulfanyl-2-methyl propionic acid, a trithiocarbonate RAFT CTA, in conjunction with the room-temperature azo initiator 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile), in DMF, at 25 degrees C, yields conditions leading to NIPAM homopolymerizations which bear all of the characteristics of a controlled/"living" polymerization. We also demonstrate facile size exclusion chromatographic analysis of PNIPAM samples in DMF at 60 degrees C, directly on aliquots withdrawn during the polymerizations, which avoids the problems previously reported in the literature.